PWODWI
Fonksyon
Nimewo CAS: | 7440-25-7 |
Estanda: | ASTM B364-92 |
Pite: | Pi gran pase oswa egal a 99.9 pousan oswa 99.95 pousan |
Gwosè: | Epesè 0.07-10 mm; Lajè 30-1000 mm; Longè 30-3000 mm |
Klas materyèl: | R05200, Tantal san alyaj, gwo founo elèktron-oswa vakyòm-ark fonn, oswa toude R05400, Tantal san alyaj, konsolidasyon metaliji poud-. |
Tantal Fèy ak Plak Deskripsyon
Fèy Tantal yo woule soti nan pi epè plak Tantal epi yo ka pli lwen woule nan mens teren & FOIL.
Tantal se yon metal ble fonse-gri tantal ki lou anpil, duktil, epi ki difisil epi ki gen gwo rezistans korozyon. Li espesyalman rezistan a pwodwi chimik nan tanperati ki anba a 150 degre epi li ka fonn sèlman ak asid fluoridrik. Li tou gen yon gwo pwen k ap fonn epi li kapab fòme kouch oksid trè mens ak pwoteksyon pou kondansateur bon jan kalite -.
SSC pwodui fèy Tantal pite segondè ak plak pou aplikasyon komèsyal ak rechèch ak pou nouvo teknoloji propriétaires. Fèy Tantal ak teren ka defòme trè byen, si wi ou non pou pwensonaj, koupe, desen gwo twou san fon oswa peze.
Nan SSC, Tantal ak pwodwi alyaj Tantal nou yo disponib tou nan fòm papye, fil, baton, riban, granules, poud, sib sputtering, disk, elatriye Nou kapab fabrike pwodwi Tantal ki anwo yo nan spesifikasyon ou ak desen. Konpozisyon koutim yo disponib tou.
Pifò dra Tantal ak plak yo pwodui nan lengote jete pou itilize nan kouch ak fim mens Depozisyon Vapè Chimik (CVD) ak pwosesis Depozisyon Vapè Fizik (PVD) ki gen ladan evaporasyon tèmik ak elektwon (E-Beam), ba tanperati òganik. Evaporasyon, Atomik Kouch Depozisyon (ALD), Organometallic ak Chimik Vapè Depozisyon (MOCVD) pou aplikasyon espesifik tankou selil gaz ak enèji solè. Materyèl yo pwodui lè l sèvi avèk kristalizasyon, eta solid ak lòt pwosesis pirifikasyon ultra wo tankou sublimasyon.
Tailor-fè fèy alyaj Tantal ak plak, tankou alyaj Tungstène Tantal, alyaj niobyòm Tantal yo disponib tou nan SSC.
Konpozisyon chimik
Eleman | C | O | N | H | Fe | Mo | Nb | Ni | Si | Ti | W |
R05200 (pousan, Max) | 0.01 | 0.015 | 0.01 | 0.0015 | 0.01 | 0.02 | 0.1 | 0.01 | 0.005 | 0.01 | 0.05 |
R05400 (pousan, Max) | 0.01 | 0.03 | 0.01 | 0.0015 | 0.01 | 0.02 | 0.1 | 0.01 | 0.005 | 0.01 | 0.05 |
Pwopriyete mekanik pou Tantal Rolling Products
Klas ak gwosè | Rekwit (tanperaman regilye) | ||
Fòs rupture Min, psi (MPa) | Sede fòs min, psi (MPa) (2 pousan) | Pwolonjman min, pousan (1 pous longè gage) | |
Fèy, papye ak plak (R05200, R05400) | |||
Epesè<0.060"> | 30000 (207) | 20000 (138) | 20 |
Epesè ki pi gran pase oswa egal a 0.060" (1.524mm) | 25000 (172) | 15000 (103) | 30 |
Ta-10W (R05255) Tantal tengstèn alyaj fèy ak plak | |||
Epesè<0.125"> | 70000 (482) | 60000 (414) | 15 |
Epesè ki pi gran pase oswa egal a 0.125" (3.175mm) | 70000 (482) | 55000 (379) | 20 |
Ta-2.5W (R05252) Tantal tengstèn alyaj fèy ak plak | |||
Epesè<0.125"> | 40000 (276) | 30000 (207) | 20 |
Epesè ki pi gran pase oswa egal a 0.125" (3.175mm) | 40000 (276) | 22000 (152) | 25 |
Ta-40Nb (R05240) Tantal niobyòm alyaj fèy ak plak | |||
Epesè<0.060"> | 40000 (276) | 20000 (138) | 25 |
Thickness>0.060" (1.524mm) | 35000 (241) | 15000 (103) | 25 |
Endistri ki gen rapò ak aplikasyon pou Tantal fèy ak plak
● Rechèch ak laboratwa
● Ranplase platinum
● Faktori superalliaj ak elektwon-fonn gwo bout bwa
● Metaliji
● Machin
● Glass
● Seramik
● Aditif superalloy nan alyaj ki baze sou nikèl{0}
● Sputtering objektif
● Zòrèy atifisyèl
● Glass oswa metal sele
● Espas
Idantifyan chimik yo
Fòmil lineyè | Ta |
Nimewo MDL | MFCD00011252 |
EC No. | 231-135-5 |
Beilstein/Reaxys No. | N/A |
Pubchem CID | 23956 |
SOURI | [Ta] |
InchI Idantifikatè | InChI=1S/Ta |
InchI kle | GUVRBAGPIYLISA-UHFFFAOYSA-N |
Fèy Tantal ak Pwopriyete Plak (teyorik)
Pwa molekilè | 180.94 |
Aparans | Solid-gri an ajan |
Pwen k ap fonn | 3017 degre |
Pwen bouyi | 5458 degre |
Dansite | 16.69 g/cm3(20 degre) |
Solibilite nan H2O | N/A |
Crystal Faz / Estrikti | : kò-santre kib (bcc) / : tetragonal |
Rezistivite elektrik | 131 nΩ·m (20 degre) |
Elektwonegativite | 1.5 Paulings |
Chalè nan fizyon | 36.57 kJ/mol |
Chalè nan Vaporizasyon | 753 kJ/mol |
Pwopòsyon Poisson a | 0.34 |
Espesifik Chalè | 140 J/kg·K |
Kondiktivite tèmik | 57.5 W/m·K |
Ekspansyon tèmik | 6.3 µm/m·K |
Vickers dite | 870-1200 MPa |
Modil Young la | 186 GPa |
Baj popilè: Tantal fèy ak plak, Lachin, Swèd, achte, pou vann, te fè nan peyi Lachin